PRi FILL

• Floors and walls,
• Floors and walls, for internal and external use
• For environments subject to heavy traffic,
• For internal and external use,
• Ideal for decorating corrected slabs
• In domestic, commercial and industrial applications
• Suitable for homogeneous tiles, ceramics, low thickness slabs and natural stone
• Swimming pools, tanks and fountains an

• Easy to clean and maintain
• High-performance grouting, from 0 to 5 mm, with extra-fine finish, high degree of hardness and reduced water absorption
• Natural bacteriostatic and fungi static.
• Single-component with very low volatile organic compound emissions, contains recycled raw materials.
• Stabilized mineral grout containing pure NHL (Natural Hydraulic Lime) 5 for extremely colour-fast joints from 0 mm to 5 mm

1. Before commencing grouting the adhesive bed must be set. It is essential that the tils used are appropriate for the service conditions and are fixed in a solid bed of adhesive i.e ensuring that, as far as possible, no voids are left behind the tiles; refer to the relevant product data sheet for setting / drying times.
2. Protect open joints from contamination and ensure that they are clean, dry and free from loose debris prior to grouting. Do not use in damp conditions

• Joint should be free efflorescence, latence, dirt and other loose material.
• Remove thoroughly by dry brushing.
• Clean all joints should be cleaned down by washing with water containing detergent, then clean water
• Ensure the joints are dry before grouting
• Movement joints should be provided in accordance with BS 5385: part 1-5 and may be filled with the appropriate flexible sealant.
• Intermediate floor joints should be reinforced with brass or stainless steel.
• Use stainless steel where hygiene is essential.

• Mix the cementitious powder with clean water until a lump-free smooth paste of uniform colour is obtained..
• If an electric drill mixer is used blend on a slow speed (less than 300 rpm)
• Avoid entraining air by mixing at too high speed or by over-mixing.
• Do not reconstitute the mixed grout by adding more water; this will reduce the final strength.

1. using a grout float or rubber squzee compact the grout into the joints ensuring that they are completely filled. Work in small areas and remove as much excess grout from the tile surface as possible. Do not exceed the working time of the grout. Refer to table for details.
2. Use a sponge or sponge-board, dampened with clean water to clean the tile surface. Allow about 15 minutes for the grout to dry a little before cleaning off.
3. Clean diagonally to the joint lines.
4. Finally wash down with clean water with sponge/sponge board to remove any dried grout film from the tile surface.
5. Once the grout has sufficiently set within the joints, polish the surface with a clean cloth.
6. Alternatively give a final wash down with clean water using a dampened sponge. The addition of TUFFEX GT to cement-based grout will enhance adhesion to tile edges, water- resistance and improves flexibility

• Do not fill pool at least 3 weeks following completion of grouting.
• Do not use on joints more than 5 mm in width, on floors and walls where specific chemical resistances or absolutely no water absorbency is required
• Do not use on substrates which are highly deformable, not fully dry or subject to moisture rising.
• Do not use showers for at least 2 weeks following completion of grouting.
• Do not use to grout elastic expansion or fractionising joints
• Not recommended for use in power showers.
• Use PRi epoxy grout which confirms to the current food hygiene regulations.
• grouts will enhance adhesion to tile edges, reduce water permeability and impart flexibility.

Always use protective gloves and eyewear both during mixing and during application avoid any contact with the eye. If in case happens do not rub, clean with plenty of fresh water immediately.